Abstract
Gold (Au) thin films with thickness of 35[Formula: see text]nm were prepared by electron beam deposition onto flat glass substrates under high vacuum [Formula: see text]Pa) condition and they were annealed in the range of 573–873 K for 1 and 2[Formula: see text]h in atmospheric pressure. The influence of the annealing temperature on the evolution of Au thin film to nano–micro particles was studied. Moreover, the basic properties of the films, namely morphological, structural and optical were investigated. The X-ray diffraction (XRD) analysis revealed that the Au thin films were cubic structure phase with lattice parameter around [Formula: see text][Formula: see text]Å. The most preferential orientation is along (111) planes for all Au films. The lattice parameter and grain size in the films were calculated by X-ray patterns and correlated with annealing temperatures. The obtained results of ultraviolet–visible spectrometry (UV–Vis) indicate that with increasing annealing temperature, the surface plasmon resonance peak of gold nanocrystallite will disappear which implies the size of particles are grown. Field-emission scanning electron microscopy (FE-SEM) results show that the prepared gold thin films have been converted to nano–micro gold particles in different annealing temperatures. These results lead to controlling the size of produced nanocrystallite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.