Abstract
To investigate whether oral cleansing agents affect the essential work of fracture (EWF) and plastic work of fracture (PWF) for two types of orthodontic thermoplastic retainer materials. Polyethylene-terephthalate-glycol (PETG; Tru-Tain Splint) and polypropylene/ethylene-propylene rubber (PP-EPR) blend (Essix-C+) sheets were compared. For each material, six sets of 25 sheets were thermoformed into double-edge-notched-tension specimens; subsets of five specimens were formed with internotch distances (L) equal to 6, 8, 10, 12, or 14 mm, respectively. Sets were stored (160 hours, 25 degrees C) in air (DRY), distilled water (DW), Original Listerine (LIS), mint Crest ProHealth (CPH), 3% hydrogen peroxide (HP), or Polident solution (POL). Specimens were fractured in tension at 2.54 mm/min. Areas under load-elongation curves were measured to determine total work of fracture (W(f)). Linear regressions (W(f) vs L [n = 25]) yielded intercepts (EWF) and slopes (PWF). Ninety-five percent confidence intervals were used to evaluate differences in EWF and PWF estimates. PP-EPR blends showed higher EWFs after storage in HP vs storage in DW. PP-EPR blend showed higher EWFs after storage in CPH vs PETG. After HP storage, PP-EPR exhibited lower PWFs than with any other storage conditions. PP-EPR exhibited higher PWFs than PETG after storage in DRY, DW, and LIS. Compared with DW, none of the cleansers decreased the energy to initiate fracture. With one exception, no cleanser decreased the energy to continue plastic fracture extension. In PP-EPR blend, increased resistance to fracture initiation was observed with CPH and HP, yet, surprisingly, HP decreased resistance to plastic fracture growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.