The equilibrium phase boundary between hexagonal and cubic boron nitride

Abstract

Abstract The equilibrium phase boundary between hexagonal and cubic boron nitride was determined over the pressure range 3–6 GPa and the temperature range 1200–2200°C. Absolute pressure and temperature were estimated based on the minimum P–T point of diamond formation in the conventional metal catalyst system using the Kennedy–Kennedy equilibrium line between graphite and diamond. Above 3.8 GPa, we determined the phase boundary by detecting the formation of cubic BN in the catalyst-containing system and by the reverse transformation from cubic BN to hexagonal BN. Below 3.8 GPa, we determined the boundary by careful observation of the transformation behavior of cubic BN powder. The rate of phase transformation from cubic BN to hexagonal BN was evaluated from the ratio of X-ray diffraction peak intensities of both phases. We found that the amount of cubic BN phase clearly changed at the phase boundary. Two sets of the results could be plotted with a uniquely determined boundary line expressed by the equation P(GPa)=T(°C)/465+0.79, which is located about 300°C higher at 5 GPa than the line determined by Bundy and Wentorf in 1963.