Abstract
Abstract The cadmium intermetallics REPtCd (RE = La, Ce, Pr, Nd, Eu) and CeAuCd were synthesized by induction-melting of the elements in sealed niobium ampoules followed by annealing in muffle furnaces. The samples were characterized by powder X-ray diffraction. The structures of CePtCd (ZrNiAl type, P 6 ¯ 2 m , $P\bar 62m,$ a = 763.8(6), c = 409.1(4) pm, wR2 = 0.0195, 298 F 2 values, 14 variables) and EuPtCd (TiNiSi type, Pnma, a = 741.3(2), b = 436.4(1), c = 858.0(4) pm, wR2 = 0.0385, 440 F 2 values, 20 variables) were refined from single-crystal data. The REPtCd structures exhibit three-dimensional networks of corner- and edge-sharing Cd@Pt2/6Pt2/3 and Cd@Pt4/4 tetrahedra, which leave cages for the rare earth atoms. Temperature-dependent magnetic susceptibility data of CeAuCd reveal a paramagnetic to antiferromagnetic phase transition at T N = 3.7(5) K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.