Abstract
The magnetic and electrical properties of La0.67Sr0.33MnO3 ( LSMO ) are influenced very much by the Nb dopant. However, this doping effect is restricted by the limited Nb solution into LSMO due to the low calcined temperature. As a result, a second phase LaNbO4 appears in our samples. Enhancements of the low-field magnetoresistance (LFMR) were observed both at 77 K and room temperature in the manganite system prepared by doping Nb2O5 into LSMO powders. The doping amount x of Nb ions ranges from 0-10 % molar ratio. The MR ratios at 77 K with H = 1 T and H = 0.1 T are 33.8 % and 24 % for the x = 0.07 doped sample, respectively. A MR effect up to 9 % was also found for the sample with x = 0.05 at room temperature, which is 2.2 times as large as that for LSMO (4.1%). The spin dependent tunneling and scattering at the interfaces of the grain boundaries are responsible for the LFMR while the high field magnetoresistance (HFMR) originates from the spin dependent transport related to noncollinear spin structure at the interfaces.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.