Abstract
0.07Pb(Sb1/2Nb1/2)O3-0.93Pb(ZrxTi1−x)O3 (PSbN-PZT) piezoceramics were fabricated at a low firing temperature of 920 °C using the LiBiO2, CuO and ZnO (LBCZ) sintering aids. The material samples exhibited excellent properties, including a converse piezoelectric coefficient d33* of ~558 pm/V, a relative dielectric permittivity εT33/ε0 of ~1725, a planar coupling factor kp of ~0.6 and a high Curie temperature Tc of ~308 °C, thus demonstrating the material suitability for use as a low-cost multilayer actuator. PSbN-PZT piezoceramic multilayer actuators with Ag/Pd internal electrodes were fabricated by tape casting method cofired at 920 °C. A large displacement of 1.45 μm was achieved in a single PSbN-PZT multilayer actuator (thickness = 2.0 mm) at the driving voltage of 125 V, while the displacement decreased ~27% under the mechanical stress of ~32 MPa. Good temperature stability was also exhibited in PSbN-PZT multilayer actuator, which was better than that of commercial PZT-5H ceramic. These results indicated that low-temperature fired PSbN-PZT multilayer actuator is a promising candidate device for commercial piezoactuator applications.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.