Abstract
Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT) ceramics were produced by using the seed-induced method. The nano-particle BZ (BaZrO3) seeds were mixed with BaCO3, CaCO3, ZrO2 and TiO2 powder for preparing by the mixed oxide method. The XRD results indicated that all powder and sintered ceramic samples showed a pure perovskite phase with coexistence between rhombohedral and tetragonal phase. As the BZ seed content increased, the density of ceramics tended to decrease from 5.61 g/cm3 to 5.37 g/cm3. The average grain size of the ceramics was in the range of 12.15 -13.50 mm. The dielectric loss (tand) was less than 0.03 for all samples at room temperature (at 1 kHz). Other electrical properties, including dielectric constant (εr), remnant polarization (Pr), and piezoelectric charge coefficient (d33) values decreased with increasing BZ seed doping with relates to the decreasing grain size and density of BCZT ceramics. However, the values of coercive field (Ec) decreased and piezoelectric voltage coefficient (g33) increased with BZ seed doping.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.