Abstract
The effects of withdrawal stop duration in the directional solidification of Al-7 wt% Si alloy on solidification parameters, microstructure, and microhardness were investigated. Directional solidification experiments were carried out in five stopping durations: 0 s, 20 s, 30 s, 40 s, and 50 s. Some solidification parameters such as growth rate and temperature gradient were calculated in the stopping region 15 mm from the bottom of the sample. Microstructure parameters such as primary and secondary dendrite arm spacings were defined on both longitudinal and transverse sections in the stopping region, whereas microhardness properties were tested on the longitudinal section in this region. With the rise in the withdrawal stop duration from 0 s to 50 s, the growth rate decreased slightly from 1.26 to 0.84 mm/s, while the temperature gradient remained at 1.71 ˚C/mm. Furthermore, the microstructure of α-Al dendrites became coarser, and their shapes changed from thin to irregular plates. Primary and secondary dendrite arm spacings increased from 106.4 to 205.7 µm and 19.4 to 38.1 µm, respectively, when the stopping duration was increased. In addition, the hardness decreased from 54.0 to 49.9 HV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.