Abstract
The objective of this study was to investigate the effects of precuring of primer coated on bracket bases on the strength of bonds between metal brackets and gold alloy. Square type III gold alloy plates were sandblasted with 30 μm silicon dioxide. After silica coating, excessive particles were removed gently with air. Silane was then applied, and maxillary central incisor metal brackets were bonded to each conditioned alloy surface with Transbond XT. Half of the specimens were precured at the bracket base after primer coating and the other half was not precured before bonding to the alloy surface. After bracket positioning, samples were cured using a light emitting diode (LED) for 40 seconds. Shear bond strengths were tested and adhesive remnant index (ARI) was evaluated after 1 hour and 24 hours. The primer precuring and 24 hours group exhibited highest bond strength (12.53 MPa) and the no precuring and 1 hour group showed lowest bond strength (5.58 MPa). Precured groups showed lower ARI scores. Due to the shallow curing depth of LED light and inhibition of transillumination at the metal surface, primer precuring at the bracket base is required for secure bracket bonding on gold alloy surfaces using LED curing units.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.