Abstract
Calcium carbide-derived carbons (CCDCs) produced by chlorination of CaC2 at various temperatures (400–800 °C) possess highly controllable microstructure and porosity, allowing them to serve as excellent electrode materials for the application of supercapacitor. This paper focused on the effect of pore size and specific surface area (SSA) of CCDC on its electrochemical behavior. Microstructure and micropore characteristics of CCDC were characterized by N2 adsorption/desorption isotherms, X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results showed that SSA and average pore size increased with the increase of synthesis temperature from 400 °C to 600 °C, and then decreased when temperature reached to 800 °C. Meanwhile, a correlation between specific capacitance and SSA of micropores (less than 2 nm in diameter) has been studied. It has been found that the supercapacitor using the CCDC prepared at 600 °C as electrode material in 6 M KOH showed the maximum specific capacitance and energy density (53.61 F g−1 and 7.08 W h kg−1), outstanding rate capability, lower IR drop and 96 % retention of initial capacity over 5,000 cycles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.