Abstract
PurposeThe influence of different light-emitting diode (LED) curing light intensities on the translucency and surface gloss of bulk-fill resin-based composite (RBC) restorative materials was evaluated.Materials and MethodsForty specimens of each RBC (Filtek One bulk-fill posterior, Reveal HD bulk, Tetric N-Ceram, and Filtek Z350) were prepared. The RBCs were shaped into molds and cured using an LED curing light unit at high intensity (1,200 mW/cm2) for 20 s and low intensity (650 mW/cm2) for 40 s. A spectrophotometer was used to determine the translucency, and a gloss meter was used to evaluate surface gloss. Data were analyzed using one- and two-way analysis of variance (ANOVA), independent t-test, and Tukey’s and Scheffe’s post hoc multiple comparison tests.ResultsThe highest translucency value was observed for Reveal HD (7.688 ± 0.861) with a high curing intensity, while Filtek One showed the lowest value (1.750 ± 0.376) with a low curing intensity. The materials showed no significant difference in surface gloss with a high curing intensity. With low-intensity light curing, Filtek One showed the highest gloss value (55.270 ± 10.106), while Tetric N-Ceram and Reveal HD showed the lowest gloss values (35.560 ± 6.533 and 35.680 ± 6.648, respectively).ConclusionCuring light intensity had no effect on both the gloss and translucency for all the materials tested, although for Tetric N-Ceram, higher intensity corresponded to higher gloss values while for Filtek One, higher intensity corresponded to a higher translucency value.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.