Abstract
The present study systematically investigated the influence of forging strategies on the microstructures and deformation behaviors of a Ti-5Al-5Mo-5V-1Cr-1Fe (Ti-55511) near β-titanium alloy. Microstructure analysis revealed that the as-cast alloy exhibited a basket-weave structure predominantly comprised of lamellar α phase. Three different forging methods were used to adjust the morphology of the primary α phase during the final two forging steps: 1) dual-phase (825 °C) + dual-phase forging (DD sample), 2) dual-phase + β single-phase (900 °C) forging (DS sample), and 3) β single-phase + dual-phase forging (SD sample). After standard heat treatment, the DD samples exhibited equiaxed αp due to sufficient deformation in dual-phase region, while DS samples transformed into lamellar shape due to αp reforming during the cooling process of the final β single-phase forging. In contrast, the SD samples displayed short-rod αp due to reforming in the single-phase region and insufficient deformation in the dual-phase region. All these αp and βt phases can hinder dislocation motion to enhance the strength. The DS sample exhibited the best combination of strength, ductility, and impact toughness. During tensile deformation, planar dislocation slip and twinning were dominant in the αp, while wave slip occurred in the βt phase. The fracture behavior transitioned from brittle to ductile after forging and heat treatment. Overall, this study offers a practical and effective method for optimizing the mechanical properties of the Ti-55511 alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.