Abstract
This study was designed to evaluate the effects of dental grinding and sandblasting on the ageing and fatigue behavior of pressureless-sintered biomedical grade Y-TZP ceramic. It was found that upon dental grinding and sandblasting, the surface of the material was heavily damaged in part plastically deformed, but the amount of transformed monoclinic zirconia was low. The partitioned tetragonal zirconia grains and pre-existing monoclinic zirconia in the ground and sandblasted surfaces hindered the propagation of the diffusion-controlled transformation during subsequent ageing. Dental grinding at a high rotation speed lowered the mean strength under static loading and the survival rate under cyclic loading. Sandblasting, in contrast, resulted in surface strengthening and substantially higher survival rate under cyclic loading. For all tested groups, about 10–15% lower survival-strength values were obtained when tested in artificial saliva, compared to dry specimens, implying that stress-assisted corrosion plays an important role in the fatigue behavior of dental zirconia.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.