The Effects of Carbon and Austenite Stabilizing Elements (Co, Cu, Ni and Mn) on the Microstructural Changes and the Creep Rupture Strength in 9-12 % Cr Ferritic Heat Resistant Steels

Abstract

Abstract This study examines the influence of carbon and austenite stabilizing elements (Ni, Mn, Co, Cu) on Laves phase precipitation, Fe2W formation, and creep rupture strength (CRS) in 9-12% Cr steels at 600-700°C. Nickel and manganese had minimal impact on Laves phase and coarse carbide formation up to 1% content. While cobalt increased Laves phase fraction at 650°C, it did not improve long-term CRS and even caused a rapid decrease in short-term CRS. Copper, on the other hand, promoted the precipitation of fine Cu-rich particles that acted as nucleation sites for Laves phase and M23C6 carbide. This resulted in a different needle-like Laves phase morphology compared to the globular type observed in nickel and cobalt alloys, leading to improved CRS in the copper alloy. Increasing carbon content from 0.1% to 0.2% effectively suppressed Laves phase formation, as confirmed by Thermo-Calc calculations. Notably, for cobalt alloys with higher tungsten content, higher carbon content (0.09% to 0.19%) improved CRS at 650°C, whereas the opposite effect was observed in nickel and nickel-manganese alloys. Copper alloys maintained improving CRS trends even with increased carbon, leading to the overall best CRS performance among the tested alloys with 0.2% carbon.