Abstract
The TiAl/Ti3Al interfacial misfit dislocations structures were investigated by TEM in Ti-45Al alloy and Ti-45Al/TiB2 composite. For TiAl with c/a = 1.02, only a single set of misfit dislocation arrays are crystallographically possible; these were observed in Ti-45Al alloy. However, the observation of three sets of misfit dislocation arrays in the Ti-45Al/TiB2 composite suggests that the occupation of octahedral sites in the TiAl structure by excess boron was responsible for a decrease in the c/a ratio leading to an increased fcc character of the TiAl at the TiAl/Ti3Al interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.