Abstract
Various types of intumescent fire retardant coatings (IFRCs) have been used to protect the substrates exposed to fire. In current study, high temperature filler Wollastonite (W) filler was used to improve fire performance of intumescent fire retardant coating. The basic ingredients of the coating were ammonium poly-phosphate (APP) as acid source, expandable graphite (EG) as carbon source, melamine (MEL) as blowing agent in epoxy binder, boric acid as additive and hardener as curing agent. In this study a range of coating formulations were developed by using different weight percentages of Wollastonite filler. The coated steel substrate samples were tested for fire performance using Bunsen burner and char expansion was measured using furnace fire test. Composition of the char was determined by X-ray diffraction (XRD) technique. The char morphology was studied using field emission scanning electron microscopy (FESEM). Results showed that Intumescent coating with addition of Wollastonite filler enhanced anti-oxidation of the char. Presence of phosphorus, calcium and silicon in char layer further improved the thermal stability of char.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.