Abstract
Si 3N 4 ceramic matrix composites reinforced by nearly unidirectionally aligned SiC whiskers have been prepared by extrusion and hot pressing. Unlike the case in traditional Si 3N 4 ceramic matrix composites reinforced by random SiC whiskers, the mechanical properties of the composites exhibit a significant dependence on whisker orientation. In the direction of whisker alignment for SiC(w)/Si 3N 4 composites, increments in bending strength and fracture toughness of 200 MPa and 3 MPa·m 1/2 are obtained respectively, compared to the values in the direction perpendicular to whisker alignment. Based on microscopic fractographic observation and micromechanics analyses, the effects of whisker orientation on toughening mechanisms are discussed. The results indicate that the whisker orientation, θ , is a decisive factor for the essential toughening mechanisms of whiskers. Only in the case of small θ and weak interface can whisker pullout occur, and whisker has maximum toughening effect. The results show that effects of whisker strengthening and toughening can be improved simultaneously through whisker oriented alignment. ©
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.