IntroductionThe aim of this study was to evaluate the effect of various mixing techniques including mechanical and manual mixing as well as the effect of ultrasonic agitation during placement on the compressive strength of mineral trioxide aggregate (MTA). MethodsTooth-colored ProRoot MTA (Dentsply Maillefer, Ballaigues, Switzerland) and white MTA Angelus (Angelus Soluções Odontologicas, Londrina, Brazil) were used. One gram of each powder was mixed with a 0.34-g aliquot of distilled water. Specimens were mixed either by mechanical mixing of capsules for 30 seconds at 4,500 rpm or by a saturation technique and the application of a condensation pressure of 3.22 MPa for 1 minute. Half of the specimens were placed in stainless steel molds and agitated using indirect ultrasonic activation. All specimens were subjected to compressive strength testing after 4 days. ResultsThe compressive strength values of ProRoot MTA were significantly greater than those of MTA Angelus (P < .05). The highest compressive strength values were recorded from ProRoot MTA samples that were mixed mechanically and placed using ultrasonic activation (mean = 101.71 MPa), whereas the lowest values were recorded for MTA Angelus samples that were mixed manually and placed without ultrasonic activation (mean = 53.47 MPa). Ultrasonically agitated groups had higher compressive strength values (P < .001). The specimens mixed mechanically had higher compressive strength values than those mixed manually (P < .05). ConclusionsThe compressive strength values of ProRoot MTA were significantly greater than those of MTA Angelus. Mechanical mixing enhanced the compressive strength of the material. Regardless of the mixing techniques applied, ultrasonic agitation improved the compressive strength of the material.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.