Abstract
The purpose of this study is to investigate the effects of Ti addition (1 and 2% Ti) and aging heat treatment on the mechanical and wear characteristics of Al-12Si-20Mg cast alloys. In preliminary studies conducted to determine the aging parameters, cast alloys were kept at 550 °C for 2 h before being quenched into water and aged at 200 °C for five different periods (3, 6, 9, 12, and 15 h). As the specimen aged for 12 h had the highest hardness value, all the specimens were aged at 200 °C for 12 h. The microstructures of the as-cast and aged specimens were analyzed using an optical microscope and a scanning electron microscope. The hardness of the investigated alloys was measured by micro-hardness test. The wear tests were carried out using the pin-on-disk model wear test apparatus, and the results were evaluated according to weight loss. According to the wear test results, the wear behavior of the investigated alloys changed depending on the aging heat treatment applied and the load. While Ti addition and the aging heat treatment applied reduce the weight loss at low loads (5 N), they increase the weight loss at higher loads (10 and 20 N).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.