Abstract
This study was conducted to determine the role of thermal treatment on the crystallinity and pore characteristics of porous ceramic, which was prepared from natural clay (NC) and chitosan (CS) biopolymer using the gel casting method. CS was used as an environmentally friendly pore-forming agent. The applied temperature treatment was based on thermal analysis (TGA/DTA) results and followed a sintering temperature of 900 to 1100 °C. The results showed that at sintering temperatures from 900 to 1000 °C, the crystallinities of the ceramic decrease (from 76.06 to 74.06%) and the crystallite size decreases (from 35.71 to 34.47 nm) while the lattice strain increases (calculated from the Full Width at Half Maximum (β) of the diffraction peak). The highest porosity of ceramic occurred at a sintering temperature of 1000 °C of 37.82 ± 0.19, but the formation of heterogeneous microstructure was observed. The resulting pore size for all temperature treatments was almost mesoporous (19.1 Å). Based on the results obtained, it is emphasized that the sintering temperature can be used to adjust the porosity and microstructure of porous ceramics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.