Abstract
When the Ti-6Al-4V alloy is overaged at 500-600°C, nanometer-sized α2 (Ti3Al) particles can be homogeneously precipitated inside a phases, thereby leading to strength improvement. Widmanstatten and equiaxed microstructures containing fine α2 (Ti3Al) particles were obtained by overaging the Ti-6Al-4V alloy. Precipitation of α2 (Ti3Al) particles was monitored using thermoelectric power measurements for different aging conditions in the Ti-6Al-4V alloy. Overaging heat treatments were conducted at 515, 545 and 575°C for different aging times. In addition, overaging samples were examined by optical microscopy, scanning electron microscopy and hardness measurements. It was found that the thermoelectric power is very sensitive to the aging process in the two studied Ti-6Al-4V structures.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.