The effect of the variation in resistivity and lifetime on the solar cells performance along the commercially grown Ga- and B-doped Czochralski ingots

Abstract

A systematic study of the variation in resistivity and lifetime on cell performance, before and after light-induced degradation (LID), was performed along the B- and Ga-doped Czochralski (Cz) ingots. Screen-printed solar cells with Al-back surface field were fabricated and analyzed from different locations on the ingots. Despite the large variation in resistivity (0.57 /spl Omega/-cm to 2.5 /spl Omega/-cm) and lifetime (100-1000 /spl mu/s) in the Ga-doped Cz ingot, the efficiency variation was found to be /spl ges/0.5%. No LID was observed in the cells fabricated from the Ga-doped ingot. In contrast with the Ga-doped ingot, the B-doped ingot showed a very tight resistivity range (0.87 /spl Omega/-cm to 1.22 /spl Omega/-cm), resulting in very tight lifetime and efficiency distributions. However, the LID effect reduced the efficiency of these B-doped cells by about 1.1% absolute. Additionally, the use of thinner substrate and higher resistivity B-doped Cz is shown to effectively reduce the LID effect.