Abstract
A Co75Cr13Pt12 intermediate magnetic layer was deposited between the (CoCrPt)97.5Nb2.5 upper magnetic layer and chromium underlayer by the magnetron sputtering technique. The effect of the thickness ratio of two magnetic layers and post-annealing treatment on the microstructure and magnetic properties of the films were investigated. The magnetic characteristics of the films were obtained by magnetic force microscopy, hysteresis loops and switching field distribution curves. Although annealing had no significant effect on the layer roughness, it rotated the easy axis of the magnetic layer towards the film plane, thereby enhanced the coercivity. The results showed an impressive effect of the magnetic intermediate layer thickness and post-annealing on the improving of coercivity through isolation of the magnetic grains. Formation of a non-magnetic halo around the magnetic grains reduced the inter-granular magnetostatic interaction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.