Abstract
A 3D dislocation dynamics study to ascertain the probable path of stage-I fatigue crack propagation across the persistent slip band (PSB) in austenitic stainless steel is presented. Cyclic plasticity and the resulting crack tip slip displacement (CTSD) are evaluated for cracks of varying length introduced at PSB-center and at two PSB-matrix interfaces. CTSD attains high value at either of the two interfaces irrespective of the proximity of crack front to the grain boundary. Further, a difference in microcrack propagation rate is also observed among the two interfaces. The present results assert microcrack propagation preferrentially along one of the two PSB-matrix interfaces rather than at the PSB-center. A pre-existing PSB dislocation structure localises the cyclic slip for crack lengths up to approximately half of the grain depth for an applied strain range of 2 × 10−4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.