Abstract
The layers based on chromium nitride were produced on the AZ91D magnesium alloy using a hybrid surface treatment. The treatment consists of nitriding of the chromium-precoated magnesium alloy. The proposed treatment yields diffusive, composite gradient-type chromium nitride layers which are diffusion-bonded to the substrate. The effect of these layers on the corrosion behavior of the AZ91D magnesium alloy was investigated by the potentiodynamic and impedance spectrometry methods. It was found that the formation of the diffusive, composite chromium nitride layers on the AZ91D alloy may result in a significant decrease of the corrosion activity measured by the corrosion potential. This effect is correlated with the layer thickness and becomes significant with relatively thin layers (less than 1 μm thick). Moreover, with the thin layers the impedance modulus is the highest and phase angle has a beneficial character.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.