Abstract
In this work, the effect of aging period on the characteristic transformation temperatures, thermodynamic parameters and structural variations of CuAlNiMn shape memory alloys were investigated. Aging was performed at above the austenite finish temperature of the un-aged specimen (120°C) for six different retention times, namely 1h, 2h, 3h, 4h, 5h and 6h. The changes in the transformation temperatures were examined by differential scanning calorimetry at different heating/cooling rates. The aging period was found to have an effect on the characteristic austenite and martensite transformation temperatures and thermodynamic parameters such as the enthalpy and entropy of alloys. High-temperature order-disorder phase transitions were determined using a differential thermal analysis, which showed that all the un-aged and aged specimens had an A2 → B2, B2 → L21 and an L21 → 9R, 18R transition. The structural analysis of the un-aged and aged specimens was performed through X-ray diffraction measurements at room temperature. The intensities of the diffraction peaks varied according to the aging time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.