Abstract
Polymer transfer films are thought to reduce friction and wear during sliding. In such cases, a continuous, uniform transfer film is thought to yield better wear performance. However, several polymers, including the thermoplastic polyetheretherketone (PEEK), do not always display this behavior. Recent works analyzing transfer film quality of PEEK resulted in no clear correlation to wear. Currently, the mechanisms for PEEK transfer film development are unknown, but there is evidence suggesting roughness orientation relative to sliding and frictional heating play key roles. In this work, the development of PEEK transfer film is explored in relation to multi-directional versus linear sliding, roughness orientation and temperature rise. Three distinct wear paths were chosen for wear tests. The transfer film of the square wear paths was analyzed using white light profilometry and imaging software to obtain the volume and area coverage by the film. The temperature rise during sliding of the bulk polymer pin was recorded with infrared camera radiometry for linear reciprocating tests. Scratch tests and chemical etching were conducted on the polymer pin surface to evaluate any directional bias or crystallinity orientation induced by sliding. It was found that wear debris and polymer chain orientation play no noticeable role in PEEK's transfer film formation. The transfer film gradient increased with frictional heating, and transfer film color changed under certain conditions. This color changed also correlated to reduced wear. This study also confirms that transfer film development is strongly dependent on roughness orientation, and its effects are examined.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.