The effect of substrate bias voltage on PbTe films deposited by magnetron sputtering

Abstract

The PbTe films were deposited onto ITO glass substrate by radio frequency magnetron sputtering. Effect of external direct current electrical field applied between substrate and target on the quality of films was investigated. Stylus surface profile, X-ray diffraction (XRD), atomic force microscope (AFM) and Fourier transform infrared spectroscopy (FTIR) were used to characterize the films. The film thickness was measured by a conventional stylus surface profile. The crystal structure and lattice parameters of films were determined by using XRD. The surface morphology of the films was measured by AFM. The absorption coefficients and optical band gaps of films were found from FTIR. The sheet resistance of the samples was measured with a four-point probe and the resistivity of the film was calculated. All the obtained films were highly textured with a strong (2 0 0) orientation. With increasing bias voltage to −30 V, the property of crystal structure, surface morphology and absorption coefficients and resistivity were improved. However, further increase of substrate bias leads to transformation of the property.