Abstract
In the present paper, the influence of partial substitution of Mn by Pd on structure, thermomagnetic properties, and phase transitions in the MnCoGe alloys was investigated. The studies of phase constitution revealed an occurrence of the orthorhombic TiNiSi-type and hexagonal Ni2Ti- type phases. Deep analysis of the XRD pattern supported by the Rietveld analysis allowed us to notice the changes in lattice parameters and quantity of recognized phases depending on the Pd content. An increase of palladium in alloy composition at the expense of manganese induced a rise in the Curie temperature. The values of ΔSM measured for the variation of external magnetic field ~5 T equaled 8.88, 23.99, 15.63, and 11.09 for Mn0.97Pd0.03CoGe, Mn0.95Pd0.05CoGe, Mn0.93Pd0.07CoGe, and Mn0.9Pd0.1CoGe alloy, respectively. The highest magnetic entropy change ΔSM was observed for samples with Pd content x = 0.05 induced by magnetostructural transformation. The analysis of the n vs. T curves allowed confirmation of the XRD and DSC results of an occurrence of the first-order magnetostructural transition in Mn0.95Pd0.05CoGe and Mn0.93Pd0.07CoGe alloys samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.