The effect of sterilization on mechanical properties of soft tissue allografts

Abstract

One major concern regarding soft tissue allograft use in surgical procedures is the risk of disease transmission. Current techniques of tissue sterilization, such as irradiation have been shown to adversely affect the mechanical properties of soft tissues. Grafts processed using Biocleanse processing (a proprietary technique developed by Regeneration Technologies to sterilize human tissues) will have better biomechanical characteristics than tissues that have been irradiated. Fifteen pairs of cadaveric Achilles tendon allografts were obtained and separated into three groups of 10 each. Three treatment groups were: Biocleanse, Irradiated, and Control (untreated). Each specimen was tested to determine the biomechanical properties of the tissue. Specimens were cyclically preloaded and then loaded to failure in tension. During testing, load, displacement, and optical strain data were captured. Following testing, the cross sectional area of the tendons was determined. Tendons in the control group were found to have a higher extrinsic stiffness (slope of the load-deformation curve, p = .005), have a higher ultimate stress (force/cross sectional area, p = .006) and higher ultimate failure load (p = .003) than irradiated grafts. Biocleanse grafts were also found to be stiffer than irradiated grafts (p = .014) yet were not found to be statistically different from either irradiated or non-irradiated grafts in terms of load to failure. Biocleanse processing seems to be a viable alternative to irradiation for Achilles tendon allografts sterilization in terms of their biomechanical properties.