Abstract
The microstructure and properties of Al-Si-Zn-Sr filler metals and brazed 6061-T6 aluminum alloy after heat treatment were studied, and the adsorption energy of Sr element on Si (111) surface was calculated. After Sr was added to Al-6Si-40Zn filler metal, its melting range remained unchanged, and the spreading wettability was improved. The microstructure mainly includes α-Al solid solution, fibrous Si, and η-Zn solid solution. Generally speaking, increasing Sr content could improve the average microhardness of brazed joints. The shear strength of the brazed joint containing Al-6Si-40Zn-0.8Sr filler metal was 134.23 MPa, which was 39.3% higher than that of the brazed joint without Sr The calculation results of adsorption energy showed that the surface of Si (111) mainly adsorbed Sr at the vacancy, which changed the growth mode of Si.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.