Abstract
Porous NiTi shape memory alloy (SMA) was fabricated by self-propagating high-temperature synthesis (SHS). With this study, a new solution treatment “solution treatment under loading” was applied to porous NiTi SMA fabricated by SHS to determine microstructural improvement regarding single phase NiTi. The effect of solution treatment under load on chemical composition, constituent phases and phase transformation behaviors of the specimens was investigated and discussed. The chemical composition of the specimens considerably changed with solution treatment under loading. Intermetallic phases such as Ti 2Ni and Ni 4Ti 3 disappeared, the density of B2(NiTi) phase increased and phase transformation temperatures sharply decreased. Porous single phase B2(NiTi) SMA with high chemical homogeneity could be obtained by the load applied during solution treatment at 1050 °C.