Abstract
The effect of samarium oxide was examined on the sintering, microstructure, and grain growth behaviors of (Co, Nb)-doped SnO2-based ceramics prepared by co-precipitation method. The sintered samples were studied through x-ray diffraction (XRD), scanning electron microscopy (SEM), and electron dispersive spectroscopy (EDS) analyses. The microstructure observations revealed that the samples were near fully dense at a sintering temperature of 1200°C for 1h. The samarium doping prevented accelerated grain growth of the SnO2-based ceramic in the final stage of the sintering. The mean grain size of the SnO2-based ceramic without Sm2O3 doping was 2.70µm, which was reduced to 0.887µm for the sample doped with 0.05mol% Sm2O3. The grain size reduction of samples doped with Sm2O3 could be attributed to the segregation of Sm2O3 at the grain boundaries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.