Abstract
Dye-sensitized solar cell (DSSC) is a photoelectrochemical solar cell that is able to convert solar energy into electrical energy. Sintering of TiO2film and soaking process of TiO2film in the dye solution have significant effect on the DSSC performance. The TiO2film was sintered at varied temperature from 200 °C to 500 °C for 60 minutes. From the efficiency test, it is found that the optimum performance of DSSC was produced when the TiO2film was sintered at 450 °C. In addition, the dye soaking temperature was evaluated from the temperature 40 °C to 50 °C for 6 hours. The optimum soaking temperature was 50 °C of DSSC with maximum efficiency at 2,621 %.