Abstract
The crack properties and toughness characteristics in AISI 316L weld metals were investigated in different chemical composition ranges of Cr and Ni contents. Three new filler wires were designed for the flux-cored arc welding (FCAW) process, and the Cr/Ni equivalent ratio and solidification mode of each weld metal was controlled. The microstructure revealed ductility-dip cracking (DDC) generated in the specimens containing <3 wt% of delta-ferrite ( δ-ferrite). Sigma ( σ) phase precipitation occurred in the weld metals heat-treated at temperatures ranging from 650 °C to 950 °C. The amount of σ in the δ-ferrite region increased significantly with increasing heat treatment time and temperature. At the highest Cr/Ni equivalent ratio, more of the σ phase of the weld metal transformed faster after heat treatment, which deteriorated the toughness. Meanwhile, less σ phase precipitation and DDC occurrence in the specimen containing <3 wt% of δ-ferrite did not affect the toughness reduction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.