Abstract
This investigation has been carried out to study the influence of extrusion process on microstructure and tensile properties of Mg-Mg2Si composite with different amounts of Si (3, 5 and 7wt.%). Microstructural examination was carried out using optical microscopy (OM). The cast specimens were extruded at 350°C at different extrusion ratios (6:1, 12:1 and 18:1). The results showed that the specimens with lower Si contents, have higher ultimate tensile strength (UTS) and tensile elongation values. Moreover, there was a considerable improvement in tensile properties for the specimens extruded with the ratio of 12:1 and 18:1 in comparison to the specimens of 6:1. This can be attributed to the significant reduction in size of primary Mg2Si particles from more than 200μm to 20μm, 10μm and 5μm after extrusion with the ratio of 6:1, 12:1 and 18:1, respectively. The highest UTS values were found to be 265MPa for extruded with 1:18 ratio of Mg-3Si composite.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call