Abstract
Spark plasma sintering (SPS) is a newly developed technique that enables poorly sinterable tin oxide powder to be fully densified. Sintering without sintering aids is of great importance when SnO2ceramics are used as electrodes in the glass melting industry and aluminum electrometallurgy. Dense and good-conductive Antimony-doped SnO2 ceramics can be achieved by SPS at a lower sintering temperature and in a shorter time. When the Sb2O3concentration is 1.0 mol%, the densities of the samples reach their maximum value, which is 98.2% of the theoretical value. When the content of Sb2O3was 2.44mol%, SnO2ceramics with densities 97.6% can be obtained at 800°C-1000°C, and the resistivity was about 5.19×10-2Ω.cm at the sintering temperature of 1000°C. Defined amount of Sb3+used in our research are beneficial to low the sintering temperature and promote the densification of SnO2ceramics