Abstract
Stress corrosion crack growth rates of 304L stainless steel after one-directionally warm-rolled along the longitudinal (L) direction were measured in oxygenated and deoxygenated pure water at 288 °C. The fracture mode is mainly intergranular in the Transverse-longitudinal (T-L) orientation specimen, while it is occasionally intergranular in the Longitudinal-transverse (L-T) orientation specimen. The crack growth rates in the T-L orientation are higher than those in the L-T orientation in both oxygenated and deoxygenated environments, which is related to the effective cracking growth path as the result of microstructural anisotropy and applied loading direction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.