Abstract
A CO2 laser was applied for dissimilar welding of Ti–15V–3Cr–3Al–3Sn (Ti–15–3) to Ti–6Al–4V (Ti–6–4) alloys. The microstructures and notched tensile strength (NTS) of the dissimilar welds were investigated in the as-welded and post-weld heat treatment (PWHT) conditions, and the results were compared with Ti–6–4 and Ti–15–3 homogeneous laser welds with the same PWHT. The results indicated that predominant α″ with a few α and β phases was formed in the as-welded fusion zone (FZ). Furthermore, the FZ hardness was susceptible to the PWHT and showed a plateau for the specimens aged in the temperature range from 426 to 482°C/4h. In comparison with the homogeneous Ti–15–3 weld under the same PWHT conditions, the dilution of Ti–15–3 with Ti–6–4 caused a slight increase in the Al equivalent (AlEQ) of the FZ, resulting in a further rise in FZ hardness. With the PWHT at/below 538°C, the dissimilar welds were associated with low NTS or high notch brittleness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.