Abstract
AbstractPoly(butylene succinate) (PBS) and polylactide (PLA) were blended in a co‐rotating twin‐screw extruder with various contents of PBS from 0 to 100 wt%. The effect of PBS content on the thermal and mechanical properties of PBS/PLA blends was investigated by using DSC, softening point measurements, a Charpy impact test and tensile testing. The Fourier transform infrared spectra showed that the polymers are immiscible, but the addition of PBS could modify the PLA structure in PBS/PLA blends by changing the content of amorphous and crystalline phases. In addition, the cold crystallization temperature of PLA in blends decreases in comparison with pure PLA, which shows that PBS could have a plasticizing effect on PLA. This is confirmed by the results of DSC analysis. The mechanical properties of the blends depend on the percentage of PBS addition. Typically, the mechanical properties of PBS/PLA blends are intermediate between the properties of the polyesters from which they are obtained. However, in some cases unexpected changes in mechanical properties of the blends were observed. For example, the elongation at break for a PBS/PLA blend containing 10 wt% PLA is higher than for pure PBS. © 2019 Society of Chemical Industry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.