Abstract
The effect of oxygen impurity on the typical characteristics of UN and (U, Pu)N fuels was investigated. The oxygen content of the samples was adjusted to ∼0.3, ∼0.6 and ∼1.0 wt%. It was confirmed from chemical, X-ray and ceramographic analyses that oxygen added to the nitrides existed in the oxide precipitates after sintering. While sinterability was observed. Furthermore, the addition of ∼1.0wt% of oxygen impurity decreased the thermal conductivities of UN and (U, Pu)N by 9–10 and 12–13% at 1000 and 1500 K, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.