Abstract
AbstractLow cycle fatigue tests were performed on Ti-24Al-11Nb titanium aluminide composite unidirectionally reinforced with SCS-6 fiber. (SCS-6 is a SiC-based fiber manufactured by Textron-SMD in Lowell, Massachusetts.) The effect of circular holes onthe fatigue life of this composite system was measured with respect to fiber orientation, temperature, and frequency. Longitudinal and transverse specimens with and without holes were tested at 26°C and 649°C at 0.33 Hz. In addition, longitudinal specimens were also tested at 30 Hz and 649°C to determine the effect of frequency.A degradation in fatigue life due to the presence of holes was observed in specimens loaded in the fiber direction (longitudinally). This effect is independent of frequency. The notch sensitivity factor, Q, associated with the reduction in life ranges from 0.33 to 0.50 over the range of temperature tested.The specimens oriented with the load axis perpendicular to the fiber direction (transverse) demonstrated no sensitivity of fatigue life to the presence of holes at room temperature but did possess a finite sensitivity at 649°C with a Q=0.45.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.