Abstract
To promote the formation and growth of nitride layer, a befitting surface nano-crystallization process was introduced as a pre-treatment of nitriding, and an optimized nitriding temperature was investigated. A modification layer with a depth of 350μm was formed by ultrasonic cold forging technology (UCFT) on AISI D2 surface. A series of plasma nitriding experiments for both treated and untreated samples were conducted at various temperatures ranging from 350°C to 550°C for 4h. The influences of nitriding temperature on the hardness, microstructure, morphology and composition of the sample surface were investigated by micro-hardness tester, optical microscope (OM), 3D profile-meter and scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The diffusion of nitrogen and the formation of nitrides were markedly improved by UCFT pre-treatment. A thicker and harder nitrided layer was formed at a high nitriding temperature. However, as the nitriding temperature increased to 550°C, a stronger sputter occurred on the sample surface. The results presents that it is an optimized process to be pre-treated by UCFT and nitriding at 520°C for 4h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.