The Effect of Multiple Antireflective Coatings and Center Thickness on Resistance of Polycarbonate Spectacle Lenses to Penetration by Pointed Missiles

Abstract

Previous work has shown that the impact resistance to blunt missiles is affected by coatings applied to either CR-39 or polycarbonate lenses. We investigated the effects of multiple antireflection (minimum angle of resolution [MAR]) coatings on the resistance of polycarbonate lenses to puncture on impact by sharp, high-speed missiles. Four groups of surfaced plano polycarbonate lenses were investigated. Two groups had a scratch-resistant (SR) coating applied to both surfaces. One of these groups had a 2-mm center thickness and the other had a 3-mm center thickness. The other two groups of 2-mm and 3-mm thick lenses had a MAR coating applied over the SR coating. The lenses were impacted by a missile consisting of an industrial sewing machine needle mounted in a cylindrical aluminum carrier. The sharp missiles were able to pierce the lenses at speeds between 29.6 m/s and 46.2 m/s. Impact resistance was lowest for the thinner lenses and lenses with a MAR coating. The effect of the MAR and lens thickness was subadditive. We have confirmed previous observations that polycarbonate lenses are more susceptible to penetration by sharp, high-speed missiles than blunt missiles. We have also found that reducing lens center thickness and applying a MAR coating further reduces the penetration resistance. Therefore, the use of 2-mm center thickness and MAR-coated polycarbonate lenses should be discouraged for industrial eye protectors where sharp missile hazards are possible.