Abstract
The ZrO2–Al2O3 (ZTA) ceramic particles reinforced iron matrix composite was a novel wear-resistance material because of their excellent toughness and hardness. However, the poor interfacial bonding property restricted the application of ZTAP/Fe composites in the harsh service condition. A continuous and uniform Ni80Cr20 coating on the ZTA ceramic surface was successfully prepared by multi-arc ion plating. The influence of NiCr coating on the interfacial character of ZTAP/Fe composites was investigated. The interface characteristics and phase constitutions of ZTAP/Fe composites were also analyzed by electron probe microanalysis (EPMA) and transmission electron microscopy (TEM). The results showed that the Ni80Cr20 coating can significantly improve the interfacial layer bonding of composites without visible defects. The diffusion of Ni and Cr and the formation of a continuous transition layer ensure the metallurgical bonding between ZTA ceramic and iron matrix. The composite N1 acquired better wear resistance than that of composite N2 without Ni80Cr20 coating, and the relative wear resistance was 1.98 times at the 55 N applied load. The interface of composite N1 was closely bonded with a transition layer, which may prevent the ceramic particles peeling off from the iron matrix during the wear process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.