Abstract
The present study is focused on the characterization of the fatigue damage features in carbon/epoxy laminates under mode-II loading conditions. To this aim, a sinusoidal cyclic load was applied to the End-Notched Flexural (ENF) specimens and the fatigue behavior of specimens was investigated. Scanning Electron Microscope (SEM) was used to identify the damage features on the fracture surface, i.e. fiber imprints, cusps, roller cusps, and striations. It was found that the fatigue damage features, such as cusps and striations, completely depended on the fatigue crack growth rate, da/dN. In addition, a linear relationship between the fatigue striation space and the strain energy release rate range (ΔGs) and the hysteresis loop area was established. The Acoustic Emission (AE) method was also employed to characterize the damage features. The obtained results showed that higher AE energy indicates larger and rougher cusps and striation features.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.