Abstract
The crystallite size of commercial ZnO nanocrystals was tuned from 22.5 to 13.8nm by ball-milling technique. X-ray diffraction patterns of mechanically milled ZnO nanocrystals reveal that milled samples possess the wurtzite-type hexagonal structure of ZnO. Increasing milling time results in the decrease of crystallite size and reduction of lattice parameters due to a slight increase of internal compressive strain and dislocation density. Scanning electron microscope images demonstrate the appearance of large agglomerated particles with ambiguous edges due to large aggregation tendency with slight variation in the particle size at milling time 8h. Analysis of the optical absorption spectra at different milling time indicates the blue shift of exciton absorption peak and optical gap photoluminescence spectra reveal that mechanical milling of ZnO NCs leads to quenching of emission intensity due to the creation of nonradiative centers via increasing thermal strain and mechanical deformation produced during the milling process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.