Abstract
The paper focuses on the analysis of microstructure and mechanical properties of the Ti alloy VT8М-1 (Ti-5.3Al-4.0Mo-1.2Zr-1.3Sn-0.2Si) in an ultrafine-grained (UFG) state subjected to a long-term annealing at a service temperature of (≤ 450°С). A rotary swaging (RS) was used to process an UFG state in the material. The precipitation of disperse silicides of S2 was observed after the deformation by RS. It has been shown that the UFG alloy retained its high level of thermal stability and enhanced mechanical properties after long-term annealing up to 500 hours. The role of disperse silicides in both strengthening and stability of mechanical properties in the alloy after long-term annealing is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.