The electrochemical corrosion mechanisms of Mg alloys were extensively studied in previous investigations of different chemical compositions, modified surface states and various electrolyte conditions. However, recent research focused on the active state of Mg dissolution, leading to unresolved effects of secondary phases adjacent to a stable α-solid solution passive layer. The present study investigates the fundamental electrochemical corrosion mechanisms of three different Laves phases with varying phase morphologies and phase fractions in the passive state of Mg-Al-Ca alloys. The microstructure was characterized by (transmission-) electron microscopy and synchrotron-based transmission X-ray microscopy. The electrochemical corrosion resistance was determined with a standard three-electrode setup and advanced in-situ flow cell measurements. A new electrochemical activity sequence (C15>C36>α-Mg>C14) was obtained, as a result of a stable passive layer formation on the α-solid solution. Furthermore, nm-scale Mg-rich precipitates were identified within the Laves phases, which tend to inhibit the corrosion kinetics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.