Abstract
Ionizing radiation is known to cause the deterioration of polymeric materials. In this study, the goal was to determine the effect of gamma and E-beam radiation on poly(lactic) acid (PLA) film at irradiation dosages of 1 to 30 kGy and on post-irradiated PLA after 9-months storage. The physical, chemical, mechanical, thermal, and permeability properties were investigated. Ionizing radiation of the commercial PLA film resulted in a decrease in molecular weight, crystallization temperature and melting temperature Tc and Tm, which suggested a degradation of PLA by irradiation. Irradiation had no effect on the color of the PLA film. The surface tension of PLA was decreased by gamma irradiation at dose of 1–10 kGy and E-beam irradiation at dose of 1–5 kGy. A decrease in the tensile strength, break elongation and elastic modulus was found for the gamma and E-beam irradiated PLA. Irradiation resulted in a decrease in water vapor and carbon dioxide permeability of PLA while there was no effect on oxygen permeability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.